Structure and electrical properties of (Mg/ZrO 2 ) 52  multilayer nanostructures

O. V. Stognei; Стогней О. В.; A. N. Smirnov; Смирнов А. Н.; A. V. Sitnikov; Ситников А. В.; M. N. Volochaev; Волочаев М. Н.

doi:10.31857/S036767652370237X

Structure and electrical properties of (Mg/ZrO₂)₅₂ multilayer nanostructures

作者: Stognei O.V.¹, Smirnov A.N.¹, Sitnikov A.V.¹, Volochaev M.N.²
隶属关系:
1. Voronezh State Technical University
2. Kirensky Institute of Physics of the Siberian Branch of the Russian Academy of Sciences
期: 卷 87, 编号 9 (2023)
页面: 1348-1354
栏目: Articles
URL: https://rjpbr.com/0367-6765/article/view/654621
DOI: https://doi.org/10.31857/S036767652370237X
EDN: https://elibrary.ru/GKJBXR
ID: 654621

如何引用文章

全文:

开放存取

##reader.subscriptionAccessGranted##
受限制的访问

订阅或者付费存取

详细
作者简介
参考
补充文件
统计

详细

Multilayer (Mg/ZrO₂)₅₂ nanostructures differing from each other in the thickness of the Mg layers and the same thickness of the ZrO₂ layers were obtained by ion-beam sputtering of two targets in an argon. The thickness of one bilayer (Mg + ZrO₂) varies from 3.6 to 8.5 nm. It was found that the use of zirconium dioxide prevented the oxidation of the magnesium phase. The presence of an electric percolation threshold was found when the morphology of magnesium layers changes (transition from discrete to continuous) as a result of an increase in the bilayer thickness. A change of the electrotransport mechanism in the (Mg/ZrO₂)₅₂ multilayer nanostructures upon passing through the percolation threshold has been established.

参考

Murray P., Orehounig D., Grosspietsch K., Carmeliet J. // Appl. Energy. 2018. V. 231. P. 1285.
Lin X., Zhu Q., Leng H. et al. // Appl. Energy. 2019. V. 250. P. 1065.
Stognei O.V., Smirnov A.N., Sitnikov A.V., Semenenko K.I. // Solid State Commun. 2021. V. 330. Art. No. 114251.
Liu Jiangwen, Fu Yiyuan, Huang Wencheng // Phys. Chem. C. 2020. V. 124. P. 6571.
Зубарев Е.Н. // УФН. 2011. Т. 181. № 5. С. 491; Zubarev E.N. // Phys. Usp. 2011. V. 54. No. 5. P. 473.
Sponchia G. et al. // J. Eur. Ceram. Soc. 2017. V. 37. P. 3393.
Francisco L., Sponchia G., Benedetti A. et al. // Ceram. Int. 2018. V. 44. No. 9. P. 10362.
Trolliard G., Benmechta R., Mercurio D. // Acta Materialia. 2007. V. 55. P. 6011.
Головин Ю.И. Керамические материалы на основе диоксида циркония. М.: Техносфера, 2018. 358 с.
Thornton J.A. // J. Vac. Sci. Tech. 1986. V. 6. No. 4. P. 3059.
Ceresoli D., Vanderbilt D. // Phys. Rev. B. 2006. V. 74. Art. No. 125108.
Platzer-Björkman C., Mongstad T., Karazhanov S. et al. // Mater. Res. Soc. Symp. Proc. 2009. V. 1210. Art. No. 315.
Ouyang L.Z., Ye S.Y., Dong H.W., Zhu M. // Appl. Phys. Lett. 2007. V. 90. Art. No. 021917.
Ouyang L., Qin F.X., Zhu M. et al. // J. Appl. Phys. 2008. V. 104. Art. No. 016110.
Pasturel M., Slaman M., Schreuders H. et al. // J. Appl. Phys. 2006. V. 100. Art. No. 023515.
Гриднев С.А., Калинин Ю.Е., Ситников А.В., Стогней О.В. Нелинейные явления в нано- и микрогетерогенных системах. М.: БИНОМ. Лаборатория знаний, 2012. 352 с.
Мотт Н., Дэвис Э. Электронные процессы в некристаллических веществах. Т. 1. М.: Мир, 1982. 368 с.