Composition and Structure of FCC-Structured High Entropy Alloys, Irradiated with Helium Ions

V. V. Uglov; Углов В. В.; E. O. Ungarbaev; Унгарбаев Е. О.; A. D. Sapar; Сапар А. Д.; M. V. Koloberdin; Колобердин М. В.; A. E. Kurahmedov; Курахмедов А. Е.; A. L. Kozlovski; Козловский А. Л.; A. E. Ryskulov; Рысқулов А. Е.; N. A. Stepanjuk; Степанюк Н. А.; S. V. Zlotski; Злоцкий С. В.; I. A. Ivanov; Иванов И. А.; K. Jin; Джин К.

doi:10.31857/S1028096023040210

Composition and Structure of FCC-Structured High Entropy Alloys, Irradiated with Helium Ions

Autores: Uglov V.V.¹, Ungarbaev E.O.², Sapar A.D.², Koloberdin M.V.², Kurahmedov A.E.², Kozlovski A.L.², Ryskulov A.E.², Stepanjuk N.A.¹, Zlotski S.V.¹, Ivanov I.A.², Jin K.³
Afiliações:
1. Belarusian State University
2. Nuclear Physics Institute of ME of the RK
3. Beijing Institute of Technology
Edição: Nº 4 (2023)
Páginas: 101-106
Seção: Articles
URL: https://rjpbr.com/1028-0960/article/view/664586
DOI: https://doi.org/10.31857/S1028096023040210
EDN: https://elibrary.ru/JGQRSK
ID: 664586

Citar

Texto integral

Acesso aberto
Acesso é fechado

Acesso está concedido
Acesso é fechado

Acesso é pago ou somente para assinantes

Resumo
Sobre autores
Bibliografia
Arquivos suplementares
Estatísticas

Resumo

In this study bulk samples of high-entropy alloys CoCrFeNi and CoCrFeMnNi, fabricated by arc melting (of pure metal powders up to 99.97%, argon atmosphere) followed by annealing (1150°C, 24 and 72 h) and cold rolling (85% decrease in thickness) were irradiated with He²⁺ ions (40 keV, fluence 2 × 10¹⁷ cm^–2). Samples of CoCrFeNi and CoCrFeMnNi are substitutional solid solutions with a close to equiatomic composition and a uniform distribution of elements over the depth of the alloys. They have a coarse grain structure with a grain size of about 80 µm for CoCrFeNi and 100 µm for CoCrFeMnNi alloys. It was revealed that the surface microstructure, phase and elemental composition of high-entropy alloys are resistant to irradiation. No traces of radiation erosion and changes in the elemental and phase composition of the alloys were found. In alloys, the dislocation density increases, which leads to a decrease in the size of coherent scattering regions, and helium bubbles are also formed, leading to an increase in compressive macrostresses. It was found that tensile microstresses prevail in irradiated CoCrFeNi alloys, while compressive stresses prevail in CoCrFeMnNi alloys. It has been found that high-entropy CoCrFeMnNi alloys with a more complex composition are more resistant to radiation damage.

Palavras-chave

high entropy alloys, ion irradiation, radiation defect formation, microstresses, macrostresses, X‑ray phase analysis.

Bibliografia

Ye Y.F., Wang Q., Lu J., Liu C.T., Yang Y. // Materials Today. 2016. V. 19. P. 349. https://www.doi.org/10.1016/j.mattod.2015.11.026
Manzoni A.M., Glatzel U. // Encyclopedia of Materials: Metals and Alloys. 2020. V. 2. P. 441. https://www.doi.org/10.1016/B978-0-12-803581-8.11774-6
Li W., Xie D., Li D., Zhang Y., Gao Y., Liaw P.K. // Prog. Mater. Sci. 2021. V. 118. P. 100777. https://www.doi.org/10.1016/j.pmatsci.2021.100777
Son S., Kim S., Kwak J., Gu G.H., Hwang D.S., Kim Y.T., Kim H.S. // Mater. Lett. 2021. V. 300. P. 130130. https://www.doi.org/10.1016/j.jmrt.2022.01.141
Yu P.F., Zhang L.J., Cheng H., Zhang H., Ma M.Z., Li Y.C., Li G., Liaw P.K., Liu R.P. // Intermetallics. 2016. V. 70. P. 82. https://www.doi.org/10.1016/j.intermet.2015.11.005
Koval N.E., Juaristi J.I., Muiño R.D., Alducin M. // J. Appl. Phys. 2020. V. 127. P. 145102. https://www.doi.org/10.1063/1.5142239
Zhang Y., Zuo T. T., Tang Z., Gao M.C., Dahmen K.A., Liaw P.K., Lu Z.P. // Prog. Mater. Sci. 2014. V. 6. P. 1. https://www.doi.org/10.1016/j.pmatsci.2013.10.001
Cantor B., Chang I.T.H., Knight P., Vincent A.J.B. // Mater. Sci. Eng. 2020. V. 375. P. 213. https://www.doi.org/10.1016/j.msea.2003.10.257
Senkov O.N., Scott J.M., Senkova S.V., Miracle D.B., Woodward C.F. // J. Alloys Compounds. 2011. V. 509. P. 6043. https://www.doi.org/10.1016/j.jallcom.2011.02.171
Karati A., Guruvidyathri K., Hariharan V.S., Murty B.S. // Scripta Materialia. 2019. V. 162. P. 465. https://www.doi.org/10.1016/j.scriptamat.2018.12.017
Pacheco V., Lindwall G., Karlsson D., Cedervall J., Fritze S., Ek G., Berastegui P., Sahlberg M., Jansson U. // Inorg. Chem. 2019. V. 58. P. 811. https://www.doi.org/10.1021/acs.inorgchem.8b02957
Xia S. Q., Wang Z., Yang T., Zhang Y. // J. Iron Steel Res. 2015. V. 22. P. 879. https://www.doi.org/10.1016/S1006-706X(15)30084-4
Jones N.G., Owen L.R. // Encyclopedia of Materials: Metals and Alloys. 2020. V. 2. P. 393. https://www.doi.org/10.1016/B978-0-12-803581-8.12124-1
Tian Y., Li L., Li J., Yang Y., Li S., Qin G. // Adv. Engineering Mater. 2021. V. 23. P. 2001514. https://www.doi.org/10.1002/adem.202001514
Lu Y., Huang H., Gao X., Ren C., Gao J., Zhang H., Zheng S., Jin Q., Zhao Y., Chenyang L., Wang T., Li T. // J. Mater. Sci. Technol. 2018. V. 35. P. 369. https://www.doi.org/10.1016/j.jmst.2018.09.034
Song H., Ma Q., Zhang W., Tian F. // J. Alloys Compounds. 2021. V. 885. P. 160944. https://www.doi.org/10.1016/j.jallcom.2021.160944
Zhang Z., Han E.H., Xiang C. // Corrosion Sci. 2021. V. 191. P. 109742. https://www.doi.org/10.1016/j.corsci.2021.109742
Murty B.S., Yeh J.-W., Ranganathan S. High-Entropy Alloy, 1st ed. Butterworth-Heinemann, 2014. 218 p.
Lee C., Chou Y., Kim G., Song G., Gao M.C., Zhang C., Chen W., Poplawsky J., Chou Y.C., Choo H., Liaw P.K. // Adv. Mater. 2020. V. 32. P. 2004029. https://www.doi.org/10.1002/adma.202004029
Рогачев А.С. // Физика металлов и металловедение. 2020. Т. 121. № 8. С. 807. https://www.doi.org/10.31857/S0015323020080094
http://www.srim.org/
Zhang Z., Armstrong D.E.J., Grant P.S. // Prog. Mater. Sci. 2022. V. 123. P. 100807. https://www.doi.org/10.1016/j.pmatsci.2021.100807