Study of magnetic and optical properties of Ni@Au nanotubes for local anti-cancer therapy

封面

如何引用文章

全文:

开放存取 开放存取
受限制的访问 ##reader.subscriptionAccessGranted##
受限制的访问 订阅或者付费存取

详细

The magnetic and optical properties of gold-coated nickel nanotubes obtained by template synthesis have been studied. A change in the relative intensity of an optical beam passing through a solution of nanotubes in a magnetic field perpendicular and parallel to the beam propagation shows the possibility of orienting nanotubes along the magnetic field. The results provide an assessment of the applicability of such nanotubes in combined photothermal and magnetomechanical anticancer therapy.

全文:

受限制的访问

作者简介

A. Anikin

Immanuel Kant Baltic Federal University

编辑信件的主要联系方式.
Email: anikinanton93@gmail.com
俄罗斯联邦, Kaliningrad, 236041

E. Shumskaya

Institute of Chemistry of New Materials of the National Academy of Sciences of Belarus

Email: anikinanton93@gmail.com
白俄罗斯, Minsk, 220141

S. Bedin

Federal Scientific Research Centre “Crystallography and Photonics” of the Russian Academy of Sciences”

Email: anikinanton93@gmail.com
俄罗斯联邦, Moscow, 119333

I. Doludenko

Federal Scientific Research Centre “Crystallography and Photonics” of the Russian Academy of Sciences”

Email: anikinanton93@gmail.com
俄罗斯联邦, Moscow, 119333

D. Khairetdinova

National University of Science and Technology “MISIS”

Email: anikinanton93@gmail.com
俄罗斯联邦, Moscow, 119049

V. Belyaev

Immanuel Kant Baltic Federal University

Email: anikinanton93@gmail.com
俄罗斯联邦, Kaliningrad, 236041

V. Rodionova

Immanuel Kant Baltic Federal University

Email: anikinanton93@gmail.com
俄罗斯联邦, Kaliningrad, 236041

L. Panina

Immanuel Kant Baltic Federal University; National University of Science and Technology “MISIS”

Email: anikinanton93@gmail.com
俄罗斯联邦, Kaliningrad, 236041; Moscow, 119049

参考

  1. Pankhurst Q.A., Connolly J., Jones S.K., Dobson J.P. // J. Phys. D. 2003. V. 36. No. 13. P. R167.
  2. Dutz S., Hergt R. // Nanotechnology. 2014. V. 25. No. 45. P. 452001.
  3. Oliveira H., Perez‐Andres E., Thevenot J. // J. Control. Release. 2013. V. 169. P. 165.
  4. Janssen X.J.A., Schellekens A.J., Van Ommering K. et al. // Biosens. Bioelectron. 2009. V. 24. No. 7. P. 1937.
  5. Maniotis N., Makridis A., Myrovali E. et al. // J. Magn. Magn. Mater. 2019. V. 470. P. 6.
  6. Novosad V., Rozhkova E.A. // Biomed. Engin. Trends Mater. Sci. 2011. P. 425.
  7. Shen Y., Wu C., Uyeda T.Q.P. et al. // Theranostics. 2017. V. 7. No. 6. P. 1735.
  8. Fung A.O., Kapadia V., Pierstorff E. et al. // J. Phys. Chem. C. 2008. V. 112. No. 39. P. 15085.
  9. Martínez-Banderas A.I., Aires A., Teran F.J. et al. // Sci. Reports. 2016. V. 6. No. 1. P. 35786.
  10. Загорский Д.Л., Долуденко И.М., Каневский В.М. и др. // Изв. РАН. Сер. физ. 2021. Т. 85. № 8. С. 10; Zagorskiy D.L., Doludenko I.M., Kanevsky V.M. et al. // Bull. Russ. Acad. Sci. Phys. 2021. V. 85. No. 8. P. 1090.
  11. Shumskaya A., Bundyukova V., Kozlovskiy A. et al. // J. Magn. Magn. Mater. 2020. V. 497. P. 165913.
  12. Zagorskiy D., Doludenko I., Zhigalina O. et al. // Membranes. 2022. V. 12. No. 2. P. 195.
  13. Kozlovskiy A.L., Korolkov I.V., Kalkabay G. et al. // J. Nanomaterials. 2017. V. 2017. P. 1.
  14. Shumskaya A., Korolkov I., Rogachev A. et al. // Colloids Surf. A. 2021. V. 626. P. 127077.
  15. Kaniukov E.Yu., Shumskaya E.E., Kutuzau M.D. et al. // Devices Meth. Measurements. 2017. V. 8. No. 3. P. 214.
  16. Espinosa A., Kolosnjaj‐Tabi J., Abou‐Hassan A. et al. // Adv. Funct. Materials. 2018. V. 28. Art. No. 1803660.
  17. Hemmer E., Benayas A., Légaré F., Vetrone F. // Nanoscale Horiz. 2016. V. 1. No. 3. P. 168.

补充文件

附件文件
动作
1. JATS XML
下载
2. Fig. 1. Results of NT synthesis: (a) optical micrograph of Ni-NT, (b) SEM image of Ni-NT located in the pores of TM, where each circle is the end of the NT; (c) SEM image of Ni-NT@Au, (d) EDA analysis of Ni-NT@Au for the spectra of nickel and gold, made on the same area.

下载 (208KB)
索引源数据
3. Fig. 2. Hysteresis loop of Ni-HT@Au powder samples.

下载 (75KB)
索引源数据
4. Fig. 3. Change in the relative intensity of the optical beam passed through the Ni-NT solution when switching on/off a constant magnetic field with a strength of 80 Oe, directed parallel (upper, orange curve) or perpendicular (lower, black curve) to the beam. The intensity is normalized by the signal level in the absence of a magnetic field, I0.

下载 (176KB)
索引源数据
5. Fig. 4. Optical density spectrum of Ni-NT (black curve) and Ni-NT@Au (orange curve) in 5% aqueous SDS solution. The NT concentration was 100 μg/ml. The inset shows a graph of the change in optical density of the Ni-NT solution over time, measured at a light wavelength of 700 nm.

下载 (116KB)
索引源数据

版权所有 © Russian Academy of Sciences, 2024